As fretting fatigue cracks are initiated at an early stage of life, the fretting fracture process is dominated by the stable growth of cracks. Hence the measurement of crack length is very important. This paper demonstrates the suitability of the DC potential drop technique for the measurement of fretting cracks. A calibration has been established for monitoring crack growth in BS L65 copper al...

modelling of crack propagation by finite element method under mixed mode conditions is of prime importance in fracture mechanics. this paper describes an application of finite element method to the analysis of mixed mode crack growth in linear elastic fracture mechanics. crack growth process is simulated by an incremental crack-extension analysis based on the maximum principal stress criterion,...

Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...

An assessment of the plasticity-induced crack-closure concept is made, in light of some of the questions that have been raised on the validity of the concept, and the assumptions that have been made concerning crack-tip damage below the crack-opening stress. The impact of using other crack-tip parameters, such as the cyclic crack-tip displacement, to model crack-growth rate behavior was studied...

In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...

Fatigue crack growth is examined in P/M 2124 aluminum alloys reinforced with SiC particles (SiCp) and whiskers (SiCw) over a wide spectrum of growth rates from 10 to 10 m per cycle. Effects of aging treatment, orientation of crack growth direction with respect to the rolling direction, mean stress (or stress ratio), and reinforcement volume percent on the fatigue crack growth threshold are inve...

The fracture and crack growth of mechanical structures is a usual phenomenon which is due to the application of tensile, cyclic loading or thermal stresses on the structure. So introducing of methods to prevent the crack growth is useful. Afterward, one of the repairing methods of crack growth, consisting to make a hole in the crack tip to elimi-nate the sharp corners, was explained. This metho...

* Corresponding author; Email: [email protected] ABSTRACT An important task in mixed-mode fracture analysis and prediction is the simulation of crack growth under mixed-mode conditions. To complete such a task, one must have (a) a computer code capable of handling the kinematics of general crack growth and determining the stress and deformation states during crack growth, and (b) a fracture crit...

in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fract...